The paper refers to hard magnetic properties of (Fe86−xNbxB14)0.88Tb0.12 bulk nanocrystalline magnets prepared using the vacuum mold suction technique. A combination of a specific chemical composition and sample preparation technology leads to a formation of dendrite grains of Tb2Fe14B hard magnetic phase. The microstructure of the obtained alloys strongly depends on both these factors. The examined alloys reveal high and ultra-high coercivity exceeding 7 T at room temperature. It was shown that the observed magnetic hardening is caused by the shape of the dendrite grains with sub-micro branches as a source of additional exchange anisotropy. Favorable hard magnetic properties occur for the alloy with 6 at.% of Nb content which corresponds to the maximum of activation enthalpy of Fe crystallization in amorphous Fe86−xNbxB14 basic alloys.
Figure optionsDownload high-quality image (195 K)Download as PowerPoint slide
Journal: Acta Materialia - Volume 98, 1 October 2015, Pages 318–326