![عکس صفحه اول مقاله: Fracture mechanics and microstructure in NiTi shape memory alloys Fracture mechanics and microstructure in NiTi shape memory alloys](/preview/png/1449602.png)
Crack extension under static loading in pseudoplastic and pseudoelastic binary NiTi shape memory alloy (SMA) compact tension (CT) specimens was examined. Two material compositions of 50.3 at.% Ni (martensitic/pseudoplastic) and 50.7 at.% Ni (austenitic/pseudoelastic) were investigated. The SMAs were characterized using differential scanning calorimetry to identify the phase transformation temperatures and tensile testing to characterize the stress–strain behavior. A miniature CT specimen was developed, which yields reliable critical fracture mechanics parameters. At 295 K, cracks propagate at similar stress intensities of 30±5MPam into martensite and pseudoelastic austenite. Integrating the miniature CT specimen into a small test device which can be fitted into a scanning electron microscope shows that this is due to cracks propagating into regions of detwinned martensite in both materials. Investigating a pseudoelastic miniature CT specimen in a synchrotron beam proves that martensite forms in front of the crack in the center of the CT specimen, i.e. under plane strain conditions.
Journal: Acta Materialia - Volume 57, Issue 4, February 2009, Pages 1015–1025