Co2+ doped TiO2 nanofibers with different doping percentages were successfully synthesized using a nonaqueous sol–gel method. X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), x-ray photoelectrons spectroscopy (XPS), FTIR and UV–vis spectroscopy were used to characterize the crystal structures, chemical states, morphologies and photocatalytic properties of Co doped TiO2 nanofibers. Co2+ doping was found to affect the phase transformation from anatase to rutile. Grain growth activation energy of 17.575 kJ/mol was obtained for the TiO2 nanofibers. The photocatalytic activities of the pure and doped nanofibers were investigated with degradation of methyl orange (MO) as a model pollutant. The degradation followed the Langmuir–Hinshelwood (L–H) kinetic model with pseudo-first-order apparent rates of 3.2×10−2, 5.3×10−2, 8.9×10−2 and 7.1×10−2 for Co doped nanofibers of Rt=0.0, 0.0025, 0.005, 0.01 (where Rt is the molar ratio of Co(OAc)2 to Ti(OiPr)4). The result showed that Co2+ doped nanostructure significantly enhanced the photocatalytic degradation of methyl orange under direct sunlight compared to pure TiO2. Rt=0.005 sample showed best sunlight photocatalytic performance among the above samples which is 2.3 times (after 30 min) efficient than that of pure nanostructure.
Natural sunlight photocatalytic activities of Co2+ doped TiO2 nanofibers were investigated with degradation of MO dye which followed the Langmuir–Hinshelwood (L–H) kinetic model. For Rt=0.005 sample, 99.9% degradation was observed after 75 min irradiation.Figure optionsDownload as PowerPoint slideHighlights
► Pure and Co2+ doped TiO2 nanofibers (average 30 nm diameter) were synthesized.
► XPS result revealed that Co2+ was incorporated in the TiO2 lattice.
► All samples show excellent sunlight photocatalytic properties.
► Co2+sample show 99.9% degradation of MO after 75 min sunlight irradiation.