YAlO3:Ce3+ powders: Synthesis, characterization, thermoluminescence and optical studies

Yttrium aluminum perovskite (YAP) is a promising high temperature ceramic material, known for its mechanical, structural and optical properties. YAP's also known as an ideal host material for solid-state lasers and phosphors. In this work, Ce3+ doped YAlO3 phosphors were synthesized by solid state reaction method, which is very suitable technique for large scale production. A prepared phosphor was characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), Scanning electron microscopy (SEM), Photoluminescence spectra and Thermoluminescence (TL) glow curve study. The starting reagents used for sample preparation are Y2O3, Al2O3 and CeO2, boric acid used as a flux. Ratio of Y:Al was 1:1 which shows perovskite structure confirmed by the X-ray diffraction (XRD) study. The entire prepared sample was studied by PL excitation and emission spectra. Prominent peak at 446 nm (blue emission) which shows broad emission spectra of photoluminescence. It proves that prepared phosphor can act as a single host for blue emission of light and can be used for display applications. Commission Internationale de I'Eclairage (CIE) techniques proves the blue emission of light (x = .148, y = .117). TL glow curve analysis of prepared phosphor shows the prominent peak at 189 °C for the variable UV exposure time and high temperature peak shows the more stability and less fading in the prepared phosphor. Kinetic data of prepared phosphor were evaluated by peak shape method for variable UV exposure time (5-25 min).