In the present work, a controlled growth of ZnO nanostructures by manipulating Zn metal ion concentration by the chelating action of ethylene diaminetetra acetic acid in hydrothermal method is studied. EDTA produces metal–chelate complex by the formation of bidentate ligand with Zn2+ in the solution and diminishes the reactivity of Zn metal cations. Concentration of EDTA in the mother solution was varied in different ranges like 3, 5 and 10 mM while retaining the zinc metal salt and the NaOH concentration the same. Three different morphologies of wurtzite structured ZnO nanostructures such as nanorods-bunch, separate/discrete uniformly sized hexagonal nanorods and tapered flower petals like shapes are achieved by 3, 5 and 10 mM strengths of EDTA, respectively. The medium concentration 5 mM of EDTA is found to have moderate control over producing ZnO nanostructures of uniform diameter and a high aspect (length to diameter) ratio. An array of vertically aligned free standing ZnO nanorods with uniform spacing is successfully achieved by the addition of 5 mM of EDTA in the mother solution and the same is studied for its fluorescence property at an excitation of 325 nm and it has exhibited a characteristic UV emission of ZnO around 383 nm.
► A peculiar chemical method for controlling the growth of ZnO nanorod is proclaimed.
► The chemical additive EDTA is used to alter the chemical ambience in the precursor.
► The chelant diminishes the reactivity of Zn2+ in solution by capturing them.
► 5 mM is the optimum strength of EDTA for the growth of high aspect ratio nano-ZnO.
Journal: Superlattices and Microstructures - Volume 50, Issue 4, October 2011, Pages 296–302