Solvothermal coating LiNi0.8Co0.15Al0.05O2 microspheres with nanoscale Li2TiO3 shell for long lifespan Li-ion battery cathode materials

• Li2TiO3 is used as coating materials for layer structured LiNi0.8Co0.15Al0.05O2 cathode.
• Solvothermal coating strategy is employed to strengthen surface coating.
• Coating layer improves the velocity of Li+ migration on electrode surface.
• Erosion from the HF and CO2 on electrode is greatly suppressed.

LiNi0.8Co0.15Al0.05O2 (NCA) microspheres covered by a nanoscale Li2TiO3-based shell were synthesized by a facile strategy based on a solvothermal pre-coating treatment combined with a post-sintering lithiation process. The morphology, structure and composition of the Li2TiO3-coated NCA samples were investigated by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), scanning scanning electron microscope (SEM) with an energy-dispersive X-ray spectroscope (EDS), and transmission electron microscopy (TEM). Owing to the complete, uniform and nanoscale Li2TiO3 coating shell, the resultant surface-modified NCA microspheres used as Li-ion battery cathode materials manifest remarkably enhanced cycling performances, attaining 94% and 84% capacity retention after 200 and 400 cycles at 0.5 C, respectively, which is much better than the pristine NCA counterpart (60% retention, 200 cycles). More impressively, the surface-modified NCA also shows an intriguing storage stability. After being stored at 30 °C for 50 days, the coated NCA-based cells are subjected to be cycled both at room and elevated temperatures, in which the aged cells can still remain 84% capacity retention after 200 cycles at 25 °C and 77% capacity retention after 200 cycles at 55 °C, respectively. All these results demonstrate that the Li2TiO3-coated LiNi0.8Co0.15Al0.05O2 microsphere is a promising cathode material for Li-ion batteries with long lifespan.

Nanoscale Li2TiO3-based shell encapsulated LiNi0.8Co0.15Al0.05O2 (NCA) microspheres are fabricated through a solvothermal pre-coating treatment combined with post-lithiation process. The surface-coated NCA as cathode materials shows a remarkably enhanced cycling performance and storage stability for long lifespan Li-ion batteries.Figure optionsDownload as PowerPoint slide