• Optically transparent rare earth (La3+) doped inclusion free KTiOPO4 single crystal was grown using TSSG method.
• Rare earth dope was determined as 0.08 wt.% of Ti from EDAX analysis.
• NLO measurements on KTiOPO4:La3+ crystals gives 11.2 mJ output intensity.
• Low conductivity of 1 × 10−4 Ω−1 cm−1 was observed for MHz frequencies.
Lanthanum doped KTP crystal was grown using high temperature top seeded solution growth technique. The 0.08 wt.% of La3+ doping was confirmed by the EDAX analysis. Structural and variation of lattice parameters by doping were investigated by X-ray diffraction. The ferroelectric hysteresis loop was traced in polar axis of grown crystal. Static high frequency dielectric permittivity, suppressed electrical conductivity, low loss tangent, increase of resistivity and modulus properties were studied for lanthanum doped KTP crystal by broad band dielectric spectroscopy. Desirable low ionic conductivity was found as 4 × 10−7 Ω−1 cm−1 in about 40 kHz frequencies.
Figure optionsDownload as PowerPoint slide
Journal: Journal of Alloys and Compounds - Volume 594, 5 May 2014, Pages 39–43