Electrical and optical properties of the mixed-valence misfit-layer compound (YbS)1.25CrS2
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
فلزات و آلیاژها
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Electrical and optical properties of the mixed-valence misfit-layer compound (YbS)1.25CrS2 Electrical and optical properties of the mixed-valence misfit-layer compound (YbS)1.25CrS2](/preview/png/1624584.png)
چکیده انگلیسی
The crystals of the new misfit-layer compound (YbS)1.25CrS2 were grown by chemical transport reaction in a closed silica ampoule. This compound is built up of alternately stacking of YbS and CrS2 layers. The dimensions of a unit cell are a1Â =Â 5.31Â Ã
, b1Â =Â 5.75Â Ã
, and c1Â =Â 10.63Â Ã
for the YbS sublattice and a2Â =Â 3.32Â Ã
, b2Â =Â 5.75Â Ã
, and c2Â =Â 10.63Â Ã
for the CrS2 sublattice. Both layers are incommensurate along the a-axis and the incommensurability parameter, which is defined by α = a2/a1, is about 0.625. It is found from the comparison of lattice parameters among a series of lanthanide misfit-layer compounds and lanthanide monosulfides that Yb is in an intermediate valence state close to trivalency rather than divalency due to charge transfer to CrS2 layers. Temperature-dependent electrical resistivity shows that the compound is a semiconductor with the activation energy of about 0.31 eV. This activation energy almost agrees with that of the acceptor levels in nonstoichiometric YbS samples. A reflectivity spectrum reveals small peaks at 0.8 and 1.1 eV, whereas an absorption spectrum exhibits a large peak at 1.1 eV. The results obtained suggest that valence fluctuation happens for Yb-like Eu in (EuS)1.173NbS2.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Alloys and Compounds - Volume 455, Issues 1â2, 8 May 2008, Pages 10-16
Journal: Journal of Alloys and Compounds - Volume 455, Issues 1â2, 8 May 2008, Pages 10-16
نویسندگان
Y. Ohno, T. Yamaguchi,