Coexistence of charge order and antiferromagnetism in (TMTTF)2SbF6: NMR study

The electronic state of (TMTTF)2SbF6 was investigated by the 1H and 13C NMR measurements. The temperature dependence of T1−1 in 1H NMR shows a sharp peak associated with the antiferromagnetic transition at TAF=6 K. The temperature dependence of T1−1 is described by the power law T2.4 below TAF. This suggests the nodal gapless spin wave excitation in antiferromagnetic phase. In 13C NMR, two sharp peaks at high temperature region, associated with the inner and the outer carbon sites in TMTTF dimer, split into four peaks below 150 K. It indicates that the charge disproportionation occurs. The degree of charge disproportionation Δρ is estimated as (0.25±0.09)e from the chemical shift difference. This value of Δρ is consistent with that obtained from the infrared spectroscopy. In the antiferromagnetic state (AFI), the observed line shape is well fitted by eight Lorentzian peaks. This suggests that the charge order with the same degree still remains in the AF state. From the line assignment, the AF staggered spin amplitude is obtained as 0.70 μB and 0.24 μB at the charge rich and the poor sites, respectively. These values corresponding to almost 1 μB per dimer are quite different from 0.11 μB of another AF (AFII) state in (TMTTF)2Br with effective higher pressure. As a result, it is understood that the antiferromagnetic staggered spin order is stabilized on the CO state in the AFI phase of (TMTTF)2SbF6.