This investigation focuses on sodium biphosphate (Na2HPO4) as corrosion inhibitor for construction steel. All the tests are carried out in a solution that simulates the composition of the pores in chloride-contaminated carbonated concrete. The carbonated solution (CS) contained Na2CO3 (0.0015 mol L−1), NaHCO3 (0.03 mol L−1) and NaCl (0.1 mol L−1), resulting in [Cl−]/[OH−]=10000. Inhibited solutions (IS20, IS60 and IS100) incorporated 20, 60, and 100 mmol L−1 Na2HPO4 respectively. These were labeled IS20, IS60 and IS100 respectively and result in [HPO42−]/[Cl−] = 0.2, 0.6, and 1. Cyclic voltammograms and anodic polarization curves were complemented with micro-Raman spectroscopy and XPS, to evaluate the surface film composition. The results show that chloride contamination promotes active corrosion. When phosphate ions are incorporated, steel becomes passive with a more positive corrosion potential (Ecorr), and pitting presents as the predominant form of localized corrosion. Raman spectra show a broad band, centred in 982 cm−1, suggesting that phosphates incorporate to the passive film. Phosphates are also present in the corrosion products. The surface film becomes more protective to pitting for the highest biphosphate content. However, after pitting no repassivation was detected. After over one month in immersion, steel remains passive in the condition IS100, with inhibition efficiency higher than 99%. In contrast, in the case of IS60 and IS20, pitting was detected.It can be concluded that phosphate ions are good candidates to be used as corrosion inhibitors for steel in chloride-contaminated concrete.
Journal: Electrochimica Acta - Volume 202, 1 June 2016, Pages 231–242