The corrosion behavior of 316L stainless steel (316L) and bulk amorphous Zr75Ti25 (AB) alloy was studied using electrochemical noise (EN) in simulated polymer electrolyte membrane fuel cell (PEMFC) conditions at 25 and 80 °C. At open circuit potential, under H2 environment, AB exhibited a higher corrosion-resistance than 316L and the contrary was observed under O2 environment. At imposed cathodic potential, under H2 environment for PEMFC anodic simulation, the reduction mechanism of 316L at 80 °C gave the most important EN signals of all other conditions. At imposed anodic potential, under O2 environment for cathodic simulation, the passive state was observed for 316L while severe localized corrosion for AB was obvious at 80 °C. It is concluded from the corrosion data of this work that in the anode environment of a PEMFC, the AB alloy could be a better candidate than 316L for bipolar plates. The contrary was observed in the simulated cathode environment.
Journal: Electrochimica Acta - Volume 52, Issue 15, 20 April 2007, Pages 5076–5085