To improve the oxidation resistance of TiAl intermetallic compound under high temperature condition, cathodic co-deposition of Al–Cr and Al–Ni alloy was carried out by constant potential control or potential pulse control in AlCl3–NaCl–KCl molten salt containing CrCl2 and/or NiCl2 at 423 K. Cathodic reduction of Ni and Cr starts at potential of 0.8 and 0.15 V versus Al/Al3+ in the molten salt, respectively. The co-deposition of Al, Cr, and Ni occurred at potentials more negative than −0.1 V to form a mixture of intermetallic compounds of Cr2Al, Ni3Al, and Al3Ni. Concentration of Cr in the deposit was enhanced to 43 at% at −0.1 V; however, concentration of Ni in the deposit was 6 at% at the same potential. The concentration of Ni further decreased with more negative potential to 1 at% at −0.4 V. The potential pulse technique enhanced the Ni concentration in the deposit to about 30 at%, due to anodic dissolution of Al content from the deposit at the higher side of potential on the potential pulse electrolysis.
Journal: Electrochimica Acta - Volume 52, Issue 7, 1 February 2007, Pages 2515–2519