The solvent extraction separation of bismuth and molybdenum from a low grade bismuth glance flotation concentrate

The main purpose of this study was to characterize and to extract bismuth and molybdenum from a low grade bismuth glance concentrate. Selective leaching of bismuth could be obtained at a temperature range 60 to 85 °C for a leaching duration of 2 h with hydrochloric acid concentration of 150 gpl, lignin calcium concentration of 0.02 gpl and using a solid–liquid ratio 1/4 g/cc. Treatment of leach liquor for the solvent extraction of bismuth with N235 showed that 8.0 × 10− 2 M N235 in kerosene, a 3 min period of equilibration and a pH 0.2 were sufficient for the extraction of Bi(III). This bismuth-loaded organic phase was almost completely stripped using 0.5 M EDTA solution. Treatment of leached residue was dealt with by roasting in the presence of slaked lime, and followed by hydrometallurgical treatment of the roasted products. In the lime roasting process, molybdenum recoveries of around 99% were achieved when an excess of 50% lime over stoichiometric requirement was roasted at 700 °C for 2 h and the calcine was leached with 4 M HCl, at 70–80 °C for 2 h. Molybdenum then was effectively extracted from the leached residual solution with N235. An optimum pH of 0.5 was determined for molybdenum extraction. From loaded solvent, this metal was easily stripped with ammonia solutions to give a pregnant solution suitable for final recovery of metal by salt precipitation. Under the optimized conditions, the ultimate recovery rate of bismuth and molybdenum was more than 99% and 98% respectively.