Test methodElevated temperature nanoindentation characterization of poly(para-phenylene vinylene) conjugated polymer films

Temperature dependent mechanical properties of poly(p-phenylene vinylene) (PPV) were investigated using quasi-static (QS) and dynamic nanoindentation (NI) at temperatures over the range of 25 to 100 °C. The reduced modulus decreased from about 4.40 GPa to 3.64 GPa over this temperature range. The plasticity indices at all measurement temperatures were lower than the critical value of 0.875, characterizing material “sink-in”, rather than “pile-up” during measurements. The plasticity index showed a non-monotonic trend, with a minimum value at around 70 °C. Analysis of indentation stress relaxation data, obtained at different temperatures, was also performed using generalized Maxwell viscoelastic models. From these analyses, a relaxation mode, with a characteristic relaxation time of approximately 0.5 s, was evident. The characteristic time remained relatively unchanged over the temperature range of 25 to 100 °C. However, the relaxation modulus associated with this mode showed the expected decrease with increase in temperature.