Designing duplex, ultrafine-grained Fe-Mn-Al-C steels by tuning phase transformation and recrystallization kinetics

A novel, lightweight Fe-25.7Mn-10.6Al-1.2C (wt.%) steel is designed by exploiting the concurrent progress of primary recrystallization and phase transformation, in order to produce an ultrafine-grained, duplex microstructure. The microstructure consists of recrystallized austenite grains surrounded by submicron-sized ferrite grains, and recovered austenite regions with preferential nano-κ-carbide precipitation. This partially recrystallized duplex microstructure demonstrates excellent strength-ductility combinations, e.g. a yield strength of 1251 MPa, an ultimate tensile strength of 1387 MPa, and a total elongation of 43%, arising from the composite response by virtue of diverging constituent strength and strain hardening behaviors.