Microstructure observations on butt joint composed of Nb3Sn CIC conductors

The observation results indicated that Nb3Sn strands and a copper sheet were butted properly at the interface of the butt joint. In addition, there were hairline cracks in the Nb3Sn layers of the strands near the interface. To investigate a cause of the crack initiation, the stresses generated in the butt joint under same conditions were analyzed using a simple model. As a result, the cracks would occur with an axial compressive stress generated by the butt joint fabrication.