Permeation of a cationic polyelectrolyte into mesoporous silica: Part 3. Using adsorption isotherms to elucidate streaming potential results

Parts 1 and 2 of this series showed that the streaming potential of silica gel particles in aqueous media can be profoundly affected by their exposure to solutions of a cationic polyelectrolyte. The extent of the change in streaming potential depended on such variables as pH, salt concentration, polyelectrolyte molecular mass and concentration, pore size, and time. However, questions arose concerning the relationship between the observed changes in streaming potential and the net amount of adsorbed polyelectrolyte. Some preliminary experiments suggested that, compared to adsorption tests, the streaming potential method may be much more sensitive to the permeation of minor amounts of oligomeric impurities into the network of mesopores in the substrate. The present article follows up on these findings, evaluating adsorption isotherms for the same systems that earlier had been examined by the streaming potential method. In contrast to the earlier work, it was possible to interpret the isotherms based on a model in which adsorbate interacts with a set of equivalent, non-interacting adsorption sites. The kinetics of adsorption were time-dependent and diffusion limited. The polymer adsorbed amount was controlled by both the pore size and the surface area. The highest adsorption amount, based on mass of the substrate, was achieved when using silica gel having an intermediate pore size (15 nm) at a relatively high solution concentration of very-low-mass polyelectrolyte. The results could be fit well to a Langmuir model of the adsorption process.

Figure optionsDownload as PowerPoint slideResearch highlights
► Polyelectrolyte adsorbed into mesoporous silica followed a distinctive log-of-time dependency.
► Highest adsorption was observed in the case of silica gel having intermediate pore size.
► A null hypothesis assuming external surface dominance of adsorption was rejected.
► The pH-dependency of adsorption was opposite to what was found by streaming potential tests.