A superhydrophobic polymerized n-octadecylsilane (PODS) surface with a highly ordered lamellar structure was obtained via a one-step solution immersion process. The PODS surface had water contact and sliding angles of 159° and ∼0°, respectively. A hydrophilic/superhydrophobic surface was then obtained by chemically bonding nano-SiO2 onto the PODS surface. This SiO2/PODS layer exhibited dew-enhancing ability, similar to that of the surface of the stenocara beetle. Vapor condensation occurring heterogeneously on the SiO2/PODS surface is proposed to explain the dew-enhancing property, and these hydrophilic/superhydrophobic surfaces may have applications in enhanced heat transfer.
Superhydrophobic polymerized n-octadecylsilane surface possesses “flower-like” morphology. The flower-like morphology consists of high-orderly layer structure according to the TEM and small angle XRD characterization.Figure optionsDownload as PowerPoint slideResearch highlights▶ The phenomenon of vapor condensed on the Superhydrophobic and intrinsic dew-enhancing surface was observed. ▶ Superhydrophobic surface with amazing water-repellency was fabricated by simplely solution process. ▶ Well ordered lamellar PODS hybrids material was obtained.
Journal: Colloids and Surfaces A: Physicochemical and Engineering Aspects - Volume 377, Issues 1–3, 5 March 2011, Pages 110–114