![عکس صفحه اول مقاله: Fine tuning of gadolinium doped ceria electrolyte nanoparticles via reverse microemulsion process Fine tuning of gadolinium doped ceria electrolyte nanoparticles via reverse microemulsion process](/preview/png/595758.png)
Gadolinium doped ceria (Gd–CeO2) nanoparticles have been synthesized by an reverse microemulsion system using cyclohexane as the oil phase, a non-ionic surfactant Igepal CO 520 and their mixed aqueous solutions of gadolinium III nitrate hexahydrate and cerium III nitrate hexahydrate as the water phase. The control of particle size was achieved by varying the water to surfactant molar ratio. The synthesized and calcined powders were characterized by thermogravimetry-differential thermal analysis (TGA-DTA), X-ray diffraction analysis (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy dispersive spectroscopy (EDS), Fourier transform infrared spectroscopy (FTIR) and Raman spectroscopy. The XRD results show that all the samples calcined at 700 °C were single phase cubic fluorite structure. The average size of the particle was found to increase with increase in water to surfactant molar ratio (R). The mean diameter of the particle for various value of R varies between 8–15 nm (SEM) and 7.5–11 nm (TEM), respectively. EDS confirm the presence of gadolinia and ceria phase in the nanopowder calcined at 700 °C. FTIR analysis was carried to monitor the elimination of residual oil and surfactant phases from the microemulsion-derived precursor and calcined powder. Raman spectroscopy and DTA evidenced the formation of a solid solution of gadolinium doped ceria at room temperature.
Journal: Colloids and Surfaces A: Physicochemical and Engineering Aspects - Volume 348, Issues 1–3, 20 September 2009, Pages 130–136