Effects of chitosan molecular weight and degree of deacetylation on the properties of gelatine-based films

The effect of chitosan molecular weight (MW) and degree of deacetylation (DD) on the physicochemical properties of gelatine-based films was studied with the goal of improving the films. Determination of the dynamic viscoelastic properties (elastic modulus G′ and viscous modulus G″) of the film-forming solutions revealed that the interactions between gelatine and chitosan were stronger in the blends made with chitosan of higher molecular weights or higher degrees of deacetylation than the blends made with lower molecular weights or degrees of deacetylation. Fish gelatine films modified with chitosan of higher molecular weights or higher degrees of deacetylation had higher tensile strengths (TS, 72.4 MPa for 550 kDa vs. 62.2 MPa for 200 kDa; 63.2 MPa for 93.6% DD vs. 38.0 MPa for 76.5% DD) and higher glass transition temperatures (Tg, 130 °C for 550 kDa vs. 108 °C for 200 kDa; 108 °C for 93.6% DD vs. 103 °C for 76.5% DD). Fourier transform infrared spectra (FTIR) and X-ray diffraction (XRD) studies indicated that gelatine and chitosan interactions determined the properties of the film. Thus, combining gelatine and chitosan may be a method for improving the physicochemical properties of gelatine films, especially when using chitosan of higher molecular weights and higher degrees of deacetylation.

Cross-section morphology of fish gelatine-based films with or without 2% chitosan (degree of deacetylation: 93.1%, molecular weight: 550 kDa).Figure optionsDownload as PowerPoint slideHighlights
► The interactions between fish gelatine and chitosan were stronger in the blends made with chitosan of higher molecular weights.
► Fish gelatine films modified with chitosan of higher degrees of deacetylation had higher tensile strengths and Tg.
► Combining gelatine and chitosan may be a method for improving the physicochemical properties of fish gelatine films.