Lithium-rich manganese oxide spinel thin films as 3Â V electrode for lithium batteries
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی شیمی
مهندسی شیمی (عمومی)
پیش نمایش صفحه اول مقاله

چکیده انگلیسی
Thin film positive electrodes of lithium-rich manganese oxide spinels were prepared by radiofrequency magnetron sputtering from a LiMn2O4 ceramic target at a total pressure close to 2 Pa. Post-annealing treatments were necessary to get well-crystallized thin films displaying interesting electrochemical performances. Raman spectrum exhibiting several well-defined bands between 296 and 635 cmâ1 is typical for the lithium-rich spinel. Based on ICP, RBS and XRD analyses, the thin films composition is close to Li1.2Mn1.8O4. The latter is also in accordance with a Mn3+/Mn4+ ratio close to 0.1 deduced from XPS measurements. Best electrochemical performance (capacity value, cycling life) between 2 V and 3.5 V vs Li+/Li was obtained for thin films annealed at 600 °C. A volumetric capacity of 52 μAh cmâ2 μmâ1 (close to about 90% of the theoretical value) was obtained at the first cycle at a C/100 regime. Contrary to most studies carried out on spinel thin films cycled in the 3 V range, no appreciable degradation of the discharge capacity was observed after few tens of cycles at room temperature, highlighting the beneficial effect of substituting 20% of Mn ions by Li ions and the presence of microvoids in thin films that limits the effect of strain generated from volume variation during the Li insertion/deinsertion process.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Electrochimica Acta - Volume 180, 20 October 2015, Pages 528-534
Journal: Electrochimica Acta - Volume 180, 20 October 2015, Pages 528-534
نویسندگان
S. Cotte, B. Pecquenard, F. Le Cras, R. Grissa, H. Martinez, L. Bourgeois,