کد مقاله | کد نشریه | سال انتشار | مقاله انگلیسی | نسخه تمام متن |
---|---|---|---|---|
6716158 | 1428742 | 2018 | 13 صفحه PDF | دانلود رایگان |
عنوان انگلیسی مقاله ISI
Optimizing compressive behavior of concrete containing fine recycled refractory brick aggregate together with calcium aluminate cement and polyvinyl alcohol fibers exposed to acidic environment
ترجمه فارسی عنوان
بهینه سازی رفتار فشاری بتن حاوی سنگ آهک بازیافت شده با سنگ آهک و آلیاژین کلسیم و الیاف الماس پی وی سی در معرض محیط اسیدی
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
خوردگی، پلی وینیل الکل، بتن فیبر، راه حل بهینه، سرعت پالس اولتراسونیک، سیمان آلومینات کلسیم، آجر نسوز خرد شده،
موضوعات مرتبط
مهندسی و علوم پایه
سایر رشته های مهندسی
مهندسی عمران و سازه
چکیده انگلیسی
Earthquake-induced structural wastes and other factors causing destruction, on one hand, and issues regarding the damaging effects of acidic environments, on the other, comprise some of the most challenging concerns of humanity, thus eliminating these challenges is one of the major goals in today's construction industry. To face this challenge, this research set out to investigate the compressive behavior of concrete containing fine recycled refractory brick aggregate together with calcium aluminate cement (CAC) and polyvinyl alcohol (PVA) fibers under an acidic environment. In order to achieve this objective, 96 fine aggregate concrete specimens were exposed to 5% sulfuric acid attack for periods of 0, 7, 21, and 63â¯days, then they were subjected to various experiments. First, to determine the extent of the specimens' corrosion, the weight variations test was conducted, then, the ultrasonic pulse velocity (UPV) test, a non-destructive concrete test to obtain the level of porosity and density, was carried out, and at the end of the experimental phase, the specimens were subjected to compressive testing after being visually inspected to examine the corrosion level. Finally, using response surface method (RSM), an optimum solution for the design parameters was presented by maximizing the compressive strength of fibrous concrete as well as making the concrete mix cost-effective. Generally, the results indicate that the specimens containing calcium aluminate cement together with PVA fibers demonstrate proper mechanical properties in terms of corrosion control against acid attack, while the specimens containing fine refractory brick aggregate showed a rather unsatisfactory performance in this regard.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Construction and Building Materials - Volume 164, 10 March 2018, Pages 837-849
Journal: Construction and Building Materials - Volume 164, 10 March 2018, Pages 837-849
نویسندگان
Mahdi Nematzadeh, Javad Dashti, Behnoud Ganjavi,