Protective properties of polyaniline and poly(aniline-co-o-anisidine) films electrosynthesized on brass

Polyaniline and poly(aniline-co-o-anisidine) films were deposited on brass (Cu40Zn). The synthesis processes of homo and copolymer film were carried out under cyclic voltammetric condition from 0.12 M aniline and 0.06 M aniline + 0.06 M o-anisidine containing 0.2 M sodium oxalate solutions. Homo and copolymer films were characterized by scanning electron microscopy (SEM). SEM images clearly show that one of the brass electrodes was covered with a black copolymer film of strongly adherent homogeneous characteristic while the other one with a porous dark green homo polymer one. The corrosion performances of coated and uncoated electrodes in 3.5% NaCl were evaluated with the help of AC impedance spectroscopy, anodic polarization plots and open circuit potential–time curves. The protective effect of homo and copolymer films formed on brass grew in parallel with extended exposure time. It was only observed with copolymer-coated electrode that changes in the charge transfer resistance of copolymer-coated electrode were related to strong adsorption of copolymer film on the brass surface which led to the formation of a protective oxide layer due to its catalytic behaviour.