Tribological properties of polymer composites with diamond-like carbon flakes

Composites of epoxy resin with diamond-like carbon (DLC) flakes were fabricated. The DLC flakes were prepared from a DLC film deposited by chemical vapor deposition on an aluminum substrate. The tribological properties of composites were evaluated in air and water environments using a reciprocating friction tester and an AISI 440C mating ball. The friction coefficient of the epoxy composite decreased from 0.90 to 0.69 in air and from 0.71 to 0.29 in water with the addition of DLC flakes. The specific wear rate of the composite also decreased from 5 × 10− 5 to 7 × 10− 6 mm3/N m in air and from 4 × 10− 5 to 4 × 10− 6 mm3/N m in water. In contrast, the wear of the mating ball increased. Furthermore, the tribological properties of DLC flakes as an additive in water were evaluated. The suspension of powdered DLC in water reduced the friction coefficient of epoxy resin against the AISI 440C mating ball. Furthermore, the wear of the resin was negligibly small, although severe abrasive wear on the mating ball was observed.