Stress corrosion cracking of a copper elbow fitting

Failure was a result of the Stress Corrosion Cracking (SCC) from the outside surface that had been placed in tension by the pipeline being chocked with a block of wood to locally raise the line above a cable tray. The active species for SCC was suspected of being Amines in the Polyurethane insulation.