Behavior of chemically deposited PbS thin films subjected to two different routes of post deposition annealing
موضوعات مرتبط
مهندسی و علوم پایه سایر رشته های مهندسی مهندسی برق و الکترونیک
پیش نمایش صفحه اول مقاله
Behavior of chemically deposited PbS thin films subjected to two different routes of post deposition annealing
چکیده انگلیسی

Lead sulfide (PbS) thin films were prepared on soda lime glass substrates at room temperature by Chemical Bath Deposition (CBD) technique. This paper reports a comparative study of characteristic properties of as-prepared PbS thin films after thermal treatment through two different routes. Studies were carried out for as-prepared as well as rapidly and gradually annealed samples at 100, 200 and 300 °C. The characterizations of the films were carried out using X-ray diffraction, scanning electron microscopy and optical measurement techniques. The structural studies confirmed the polycrystalline nature and the cubic structure of the films. As-deposited films partly transformed to Pb2O3 when gradually annealed to 300 °C. The presence of nano crystallites was revealed by structural and optical absorption measurements. The values of average crystallite size were found to be in the range 18–20 nm. The variation in the microstructure, thickness, grain size, micro strain and optical band gap on two types of annealing were compared and analyzed. Data showed that post deposition parameters and thermal treatment strongly influence the optical properties of PbS films. Optical band gap of the film gets modified remarkably on annealing. Direct band gap energy values for rapidly and gradually annealed samples varied in the range of 1.68–2.01 eV and 1.68–2.12 eV respectively. Thus we were succeeded in tailoring direct band gap energies by post deposition annealing method.

ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials Science in Semiconductor Processing - Volume 16, Issue 3, June 2013, Pages 605–611
نویسندگان
, ,