Effect of NaOH solution on surface textured ZnO: Al films prepared by pulsed direct current magnetron sputtering

Transparent conducting Al-doped ZnO (ZnO:Al, AZO) thin films were prepared at substrate temperature of 270 °C by pulsed direct current magnetron sputtering. NaOH solution (5 wt%) was employed to etch the AZO films at room temperature, and the surface textured AZO films were obtained successfully. The relationship between the surface textured structures and the etching process controlled by etching time was discussed. The textured morphology of the etched AZO films became clear as increasing the etching time, and the AZO film etched for 30 min exhibited uniformly and distinctly crater-like surface textured structure. Correspondingly, the haze and the resistivity increased with the increasing etching time. And the resistivity of the AZO film etched for 30 min was 3.2×10−3 Ω cm.