• Mesoporous graphitic carbon nitride was prepared using FDU-12 as a template.
• CN-FDU-12 has a large pore size of 7.5 nm with ordered mesostructures.
• CN-FDU-12 demonstrated superior catalytic activity to CN-SBA-15 and CN-MCF.
Mesoporous g-CN material has been prepared by using FDU-12 as a template, and carbon tetrachloride and ethylenediamine as precursors via a nanocasting method. Small angle X-ray scattering and transmission electron microscopy confirm that the synthesized CN-FDU-12 possesses well-ordered mesostructures and faithfully replicates the face-centered cubic symmetry of FDU-12. The surface area and pore volume acquired in CN-FDU-12 are 702 m2 g−1 and 1.4 cm3 g−1, respectively, along with large pore size of 7.5 nm. Fourier transform infrared and X-ray photoelectron spectra reveal that the motifs of CN-FDU-12 are pyridine rings interconnected by tertiary N atoms. As a heterogeneous base catalyst, CN-FDU-12 demonstrates high and steady activity in the transesterification of ethylacetoacetate with a series of alcohols. Moreover, the catalytic activity achieved over CN-FDU-12 is superior to those obtained over other mesoporous g-CN materials templated by SBA-15 and MCF. The excellent performance is attributed to the high percentage of tertiary N species in CN-FDU-12. Accordingly, a possible reaction mechanism for the transesterification of β-keto esters has been proposed.
Figure optionsDownload as PowerPoint slide
Journal: Microporous and Mesoporous Materials - Volume 198, 1 November 2014, Pages 223–229