Dynamic tension-compression asymmetry of martensitic transformation in austenitic Fe-(0.4, 1.0)C-18Mn steels for cryogenic applications
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
سرامیک و کامپوزیت
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
In this study, cryogenic-temperature dynamic mechanical properties of austenitic Fe-(0.4, 1.0)C-18Mn steels were evaluated by conducting dynamic tensile and compressive tests, and deformation mechanisms including tension-compression asymmetry of martensitic transformation behavior were interpreted by microstructural evolution of dynamically tensioned or compressed specimens. After the dynamic tensile test of the 0.4C-18Mn steel, the γ â É â αⲠmartensitic transformation occurred at â196 °C, whereas É- or αâ²-martensite was not found in the 1.0C-18Mn steel. After the dynamic compressive test, on the other hand, the γ âÂ É martensitic transformation occurred at â196 °C without the formation of αâ²-martensites in the 0.4C-18Mn steel. This dynamic tensile-compressive asymmetry of martensitic transformation was plausibly interpreted by austenite stability in relation with difference in molar volume, hydrostatic stress distribution, and adiabatic heating. The γ â αⲠtransformation was prevented under the dynamic compressive loading because the increase in molar volume was required for the γ â αⲠtransformation, whereas it was promoted to induce the γ â É â αⲠtransformation under dynamic tensile loading.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Acta Materialia - Volume 96, 1 September 2015, Pages 37-46
Journal: Acta Materialia - Volume 96, 1 September 2015, Pages 37-46
نویسندگان
Hyunmin Kim, Jaeyoung Park, Yumi Ha, Wooyeol Kim, Seok Su Sohn, Hyoung Seop Kim, Byeong-Joo Lee, Nack J. Kim, Sunghak Lee,