Microstructural extremes and the transition from fatigue crack initiation to small crack growth in a polycrystalline nickel-base superalloy
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
سرامیک و کامپوزیت
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Microstructural extremes and the transition from fatigue crack initiation to small crack growth in a polycrystalline nickel-base superalloy Microstructural extremes and the transition from fatigue crack initiation to small crack growth in a polycrystalline nickel-base superalloy](/preview/png/7883020.png)
چکیده انگلیسی
The fatigue behavior of the nickel-base superalloy René 88 DT has been investigated at room temperature with fully reversed loading in an ultrasonic fatigue apparatus operating at a frequency close to 20 kHz. A characterization protocol based on the electron backscatter diffraction technique has been developed to identify the combination of microstructural features within crack initiation sites and surrounding neighborhoods that leads to the transition from initiation to early small crack growth. Surface grains that were more than three times the average grain size, that were favorably oriented for cyclic slip localization and that also contained Σ3 twin boundaries inclined to the loading axis were most favorable for fatigue crack initiation. Fatigue cracks subsequently grew in grain clusters within which grains are misoriented by less than 20° relative to the initiation grains. More highly misoriented neighboring grains resulted in crack arrest. The material characteristics that promote crack initiation and small crack growth exist only at the extreme tails of the microstructural distributions. The implications for modeling of fatigue life and fatigue life variability are discussed.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Acta Materialia - Volume 60, Issues 6â7, April 2012, Pages 2840-2854
Journal: Acta Materialia - Volume 60, Issues 6â7, April 2012, Pages 2840-2854
نویسندگان
Jiashi Miao, Tresa M. Pollock, J. Wayne Jones,