High-temperature synthesis of stable ordered mesoporous silica materials using mesoporous carbon as a hard template
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی شیمی
کاتالیزور
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: High-temperature synthesis of stable ordered mesoporous silica materials using mesoporous carbon as a hard template High-temperature synthesis of stable ordered mesoporous silica materials using mesoporous carbon as a hard template](/preview/png/9617519.png)
چکیده انگلیسی
Replicated mesoporous silica materials from CMK-3 (denoted as RSC-3-X, X stands for synthesis temperature) have been successfully synthesized in acidic media at high temperatures (160-240 °C) and subsequently characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), nitrogen sorption isotherms, and 29Si nuclear magnetic resonance (NMR) spectroscopy. XRD patterns and nitrogen sorption isotherms exhibit the highly hydrothermal stable mesostructure of RSC-3 samples. Transmission electron microscopy images of RSC-3-220 show ordered hexagonal arrays of mesopores with 1D channels and further confirm the 2D hexagonal (p6mm) mesostructure of RSC-3-220. 29Si MAS NMR spectra indicate that as-synthesized RSC-3 samples are primarily made up of fully condensed Q4 silica units (δ = â112 ppm) with a small contribution from incompletely cross-linked Q3 (δ = â102 ppm) as deduced from the high Q4/Q3 ratio of 5.5-9.5, implying the fully condensed walls of RSC-3. Such unique structural features should be attributed directly to the high-temperature synthesis, which could be responsible for the observed highly hydrothermal stability of RSC-3.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Microporous and Mesoporous Materials - Volume 86, Issues 1â3, 28 November 2005, Pages 81-88
Journal: Microporous and Mesoporous Materials - Volume 86, Issues 1â3, 28 November 2005, Pages 81-88
نویسندگان
Lifeng Wang, Kaifeng Lin, Yan Di, Daliang Zhang, Caijin Li, Qing Yang, Chengyang Yin, Zhenhua Sun, Dazhen Jiang, Feng-Shou Xiao,