Transport and optical properties of heavily hole-doped semiconductors BaCu2Se2 and BaCu2Te2

Experimental and theoretical studies of the electronic and optical properties of orthorhombic BaCu2Se2 and BaCu2Te2 are reported. Experimental data include the electrical resistivity, Hall coefficient, Seebeck coefficient, thermal conductivity, and lattice constants for T≤300K, and optical transmission and diffuse reflectance data at room temperature. Nominally stoichiometric, polycrystalline samples form with hole concentrations inferred from Hall measurements of 2×1018 and 5×1019 cm−3 near room temperature for the selenide and telluride, respectively. The corresponding mobilities are near 15 cm2 V−1 s−1 for both materials. Optical measurements reveal a transition near 1.8 eV in BaCu2Se2, while no similar feature was observed for BaCu2Te2. First principles calculations indicate both materials are direct or nearly direct gap semiconductors with calculated gaps near 1.0 eV and 1.3 eV for the telluride and selenide, respectively, and predict weak absorption below about 2 eV. Transport properties calculated from the electronic structure are also presented.

Combined experimental and theoretical study of orthorhombic BaCu2Se2 and BaCu2Te2 to assess potential for photovoltaic and thermoelectric applications.Figure optionsDownload as PowerPoint slideHighlights
► Comparative experimental and theoretical study of orthorhombic BaCu2Se2 and BaCu2Te2.
► Measured and calculated optical and transport properties.
► Temperature dependence of lattice parameters and transport properties.
► Hall and Seebeck coefficient measurements indicate heavy hole doping.
► Good agreement between measured and modeled room temperature Seebeck coefficients.