Novel light-cured resins and composites with improved physicochemical properties

ObjectivesThe aim of this study was to determine the effect of two new diluent agents (Bis-GMA analogues), at different dilution levels and filler contents on relevant physicochemical properties of several novel resins and composites containing Bis-GMA as matrix. Composites using TEGDMA as diluent were used as control.MethodsTwenty formulations were prepared combining three monomer mixtures (Bis-GMA/TEGDMA, Bis-GMA/CH3 Bis-GMA and Bis-GMA/CF3 Bis-GMA), at three dilution levels (85/15, 10/90, 0/100) and two percentages of filler loading (silanated barium aluminosilicate glass): 0%, 10%, 35%. Preliminary rheological testing was performed in order to obtain the viscosity of the resin samples. Resins and composites were then inserted into molds and light-cured (500 mW/cm2). The properties evaluated were: (1) homogeneity of curing (HC), using FTIR or Vickers microindentor, (2) microhardness, by a Vickers microindentor, (3) depths of cure and oxygen inhibitor effect (OIE), quantified by scraping, (4) water contact angle on the materials surface, (5) water sorption and solubility, performed by the Öysaed–Ruyter method and (6) scanning electron microscopy analysis of the specimens surfaces. Data were analyzed by ANOVA and Student–Newman–Keuls tests (p < 0.05).ResultsMaterials with CH3 Bis-GMA and CF3 Bis-GMA exhibited less hydrophilicity, water sorption and solubility. Bis-GMA dilution induced an increase in depth of cure and promoted a higher OIE, particularly when the diluent was TEGDMA. Filler loading reduced the OIE and increased hydrophobicity of the resins.SignificanceCH3 Bis-GMA may be considered as good candidate to be used as diluent because when replacing TEGDMA-induced lower hydrolytic degradation and increase in HC.