The nanopatterned c-plane sapphire substrate with different morphologies can be successfully used to grow polar and nonpolar GaN epilayers. The nanopattern of sapphire substrate was prepared with natural lithography and dry-etching methods and the following GaN epilayer was grown by MOCVD. The GaN crystal orientation and crystalline quality were then characterized by high resolution X-ray diffraction, which reveals the GaN epilayer can be c-plane (0001) or m-plane (101̄0) orientation depending on the surface morphology of nanopatterned sapphire substrate. The corresponding full width at half maximum of the rocking curves for c- and m-plane GaN are 211 and 316 arcsec, respectively. The rms surface roughness was measured to be 0.3 nm by atomic force microscopy. The atomic structure of the sapphire-GaN heterointerface was studied by high resolution transmission electron microscope to reveal the growth mechanism. Furthermore, photoluminescence, time-resolved photoluminescence, and polarization Raman spectroscopy were employed to realize the optical and structural properties of these GaN epilayers.
► High crystalline quality polar and nonpolar GaN epilayers were grown on c-NPSS.
► The crystalline qualities were examined by XRD, TEM, PL, TRPL, and Raman spectroscopy.
► The FWHM of the XRC for c- and m-plane GaN are 211 and 316 arcsec, respectively.
► The rms surface roughness is 0.3 nm measured by AFM.
► The c-NPSS can be a novel template for growing polar and nonpolar GaN epilayers.
Journal: Journal of Crystal Growth - Volume 348, Issue 1, 1 June 2012, Pages 47–52