Fabrication of synthetic calcite–muscovite rocks with variable texture — An analogue to cataclasite fabrics?

A series of large diameter calcite–muscovite aggregates has been prepared from calcite and muscovite powders, in order to gain a better understanding of how texture develops in impure carbonate rocks. The development of the microstructure and the crystallographic preferred orientation (CPO, texture) during the preparation process is described. The synthetic rocks have been fabricated from powders of calcite and muscovite by uniaxial cold-pressing at loads up to 400 MPa and subsequent hot isostatic pressing (HIPping) at pressures of 150 to 170 MPa and a temperature of 670 °C. The resulting textures and microstructures are homogeneous throughout the samples. The calcite CPO is generated by rigid body rotation and twinning during cold-pressing and is not significantly altered by recrystallization during HIPping. Grain growth during HIPping is observed in pure calcite samples, but is inhibited through high porosity and the presence of muscovite in the mixed aggregates. The preferred orientation of the calcite c-axes is found to increase with increasing uniaxial cold pressure, and to be independent of the muscovite content. The magnetic bulk susceptibility of the starting material has been changed by the formation of ferromagnetic impurities during fabrication. Comparison of the samples to natural calcite fabrics from fault zones show the potential of the experiments and fabric analyses presented to analyze and to better understand the deformation mechanisms of fault zones.