Improving electrical characteristics of W/HfO2/In0.53Ga0.47As gate stacks by altering deposition techniques

The effects of controlling InGaAs substrate temperature during electron beam deposition of HfO2 on electrical characteristics of W/HfO2/n-In0.53Ga0.47As capacitors are investigated. It is found that by depositing a thin HfO2 layer at the interface when substrate temperature is raised to 300 °C, frequency dispersion at depletion and accumulation conditions is reduced and interface state density is lowered regardless of the HfO2 thickness. Cross-sectional transmission electron microscopy images have revealed that the formation of mesoscopic voids in the InGaAs substrate near the interface is suppressed with HfO2deposition at 300 °C at the interface. A band diagram with an additional bulk trap energy level has been proposed to explain the frequency dispersion and conductance peaks at accumulation condition.

The effects of controlling InGaAs substrate temperature during electron beam deposition of HfO2 on electrical characteristics of W/HfO2/n-In0.53Ga0.47As capacitors are investigated. It is found that by depositing a thin HfO2 layer at the interface when substrate temperature is raised to 300 °C, frequency dispersion at depletion and accumulation conditions is reduced and interface state density is lowered regardless of the HfO2 thickness. Cross-sectional transmission electron microscopy images have revealed that the formation of mesoscopic voids in the InGaAs substrate near the interface is suppressed with HfO2deposition at 300 °C at the interface. A band diagram with an additional bulk trap energy level has been proposed to explain the frequency dispersion and conductance peaks at accumulation condition.Figure optionsDownload as PowerPoint slide