An investigation of the effects of radiation exposure on stability constraints in epitaxial SiGe strained layers

The thermodynamic stability of device-relevant epitaxial SiGe strained layers under proton irradiation is investigated using X-ray diffraction techniques, and compared with its stability constrain under high-temperature annealing. Irradiation with 63 MeV protons is found to introduce no significant microdefects into the SiGe thin films, regardless of starting stability condition of the SiGe film, and thus does not appear to be an issue for the use of SiGe HBT technology in emerging space systems. The strain relaxation of SiGe thin film under thermal annealing, however, is sensitive to the composition and thickness of the as-grown samples, as expected, with the subsequent lattice relaxation of the unstable samples occurring at a much higher rate than that of metastable samples.