Influence of growth parameters on the composition and impurity levels of intrinsically carbon doped AlxGa1âxAs
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
فیزیک و نجوم
فیزیک ماده چگال
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
Intrinsically carbon doped AlxGa1âxAs was grown by metalorganic chemical vapor deposition (MOCVD). The influence of the growth temperature, the V/III ratio and the aluminum fraction on the carbon, hydrogen, oxygen and aluminum incorporation was investigated over a wide parameter range. Secondary ion mass spectroscopy (SIMS) analysis was correlated with capacitance voltage (CV) measurements. It was found that a reduction of the growth temperature and the V/III ratio results in a strong decrease of the incorporated aluminum fraction in the layer, in particular in the range suitable for intrinsic carbon doping. This was explained by a lower decomposition rate of trimethyl aluminum compared to trimethyl gallium. For almost the entire investigated parameter range the carbon levels in the layer exceeded the carrier concentration due to deactivation by hydrogen and carbon incorporation on Ga-, Al- or interstitial sites. At a growth temperature of 530 °C, however, all incorporated carbon is active, even at a maximal carrier concentration of 1.7Ã1020 cmâ3. With the results obtained from this study, the carbon concentration and the aluminum fraction of intrinsic carbon doped layers can be controlled for a large range of growth conditions.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Crystal Growth - Volume 284, Issues 1â2, 15 October 2005, Pages 28-38
Journal: Journal of Crystal Growth - Volume 284, Issues 1â2, 15 October 2005, Pages 28-38
نویسندگان
J. van Deelen, G.J. Bauhuis, J.J. Schermer, P.K. Larsen,