• FeCo-reduced graphene oxide composite film was fabricated on indium tin oxide substrate.
• One step electrodeposition method was used.
• Good soft magnetic properties were exhibited by the composite films.
• Increase of resonance frequency from 2.15 GHz for FeCo film to 3.9 GHz for composite film
FeCo-reduced graphene oxide (FeCo-RGO) composite film was fabricated on indium tin oxide substrate using one-step electrodeposition method. Raman spectroscopy and field emission scanning electron microscope results show that the reduced graphene oxide is coprecipitated with the FeCo film. The energy-dispersive spectrometer results demonstrate that the atomic ratio of Fe/Co in FeCo-RGO composite film is larger than that of the FeCo film under the same fabrication condition. As a result, the FeCo-RGO composite film exhibits good soft magnetic properties and high-frequency properties as well as the FeCo film. The magnetic anisotropy field and saturation magnetization of FeCo-RGO composite film are increased when compared with FeCo film. Furthermore, the ferromagnetic resonance frequency is improved from 2.15 GHz for the FeCo film to 3.9 GHz for the FeCo-RGO composite film.
Journal: Thin Solid Films - Volume 597, 31 December 2015, Pages 1–6