عنوان انگلیسی مقاله ISI
Highly ordered nanotubular film formation on Ti-25Nb-xZr and Ti-25Ta-xHf
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
فناوری نانو (نانو تکنولوژی)
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Highly ordered nanotubular film formation on Ti-25Nb-xZr and Ti-25Ta-xHf Highly ordered nanotubular film formation on Ti-25Nb-xZr and Ti-25Ta-xHf](/preview/png/1664512.png)
چکیده انگلیسی
The purpose of this study was to investigate the highly ordered nanotubular film formation on Ti-25Nb-xZr and Ti-25Ta-xHf, examining the roles of niobium, zirconium, tantalum and hafnium alloying elements. The Ti-25Nb-xZr and Ti-25Ta-xHf ternary alloys contained 0, 7 and 15 wt.% of these alloying elements and were manufactured using a vacuum arc-melting furnace. Cast ingots of the alloys were homogenized in Ar atmosphere at 1050 °C for 2 h, followed by quenching into ice water. Formation of nanotubular films was achieved by an electrochemical method in 1 M H3PO4 + 0.8 wt.% NaF at 30 V and 1 h for the Ti-25Nb-xZr alloys and 2 h for the Ti-25Ta-xHf alloys. Microstructures of the Ti-25Ta-xHf alloys transformed from αⳠphase to β phase, changing from a needle-like structure to an equiaxed structure as the Hf content increased. In a similar manner, the needle-like structure of the Ti-25Nb-xZr alloys transformed to an equiaxed structure as the Zr content increased. Highly ordered nanotubes formed on the Ti-25Ta-15Hf and Ti-25Nb-15Zr alloys compared to the other alloys, and the nanotube layer thickness on Ti-25Ta-15Hf and Ti-25Nb-15Zr was greater than for the other alloys. Nanotubes formed on Ti-25Ta-15Hf and Ti-25Nb-15Zr showed two sizes of highly ordered structures. The diameters of the large nanotubes decreased and the diameters of the small nanotubes increased as Zr and Hf contents increased. It was found that the layer thickness, diameter, surface density and growth rate of nanotubes on the Ti-25Ta-xHf and Ti-25Nb-xZr alloys can be controlled by varying the Hf and Zr contents. X-ray diffraction analyses revealed only weak peaks for crystalline anatase or rutile TiO2 phases from the nanotubes on the Ti-25Nb-xZr and Ti-25Ta-xHf alloys, indicating a largely amorphous condition.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Thin Solid Films - Volume 596, 1 December 2015, Pages 94-100
Journal: Thin Solid Films - Volume 596, 1 December 2015, Pages 94-100
نویسندگان
Jeong-Jae Kim, In-Seop Byeon, William A. Brantley, Han-Cheol Choe,