Epitaxial YBa2Cu3O7/La0.7Ca0.3MnO3 (YBCO/LCMO) bi-layers and La0.7Ca0.3MnO3/YBa2Cu3O7 (LCMO/YBCO) bi-layers were grown on (001)LaAlO3 by pulsed laser deposition, and their microstructures were compared by transmission electron microscopy investigation. In the YBCO(100 nm)/LCMO(150 nm) bi-layers, the LCMO layer consists of columnar grains of ~ 17 nm in diameter and contains mixed orientation domains of [100]c, [010]c and [001]c. The YBCO layer is totally c-axis oriented and the YBCO lattices are tilted − 2.5° to + 2.5° as they grew on the rough surfaces of LCMO columnar grains. For the LCMO(140 nm)/YBCO(140 nm) bi-layers, the LCMO/YBCO interface is sharp and flat. The initial 12-nm thickness of the YBCO layer is composed of c-axis oriented domains, and the upper part of YBCO layer is [100] oriented. The LCMO layer was predominantly [001]c oriented while [100]c-oriented domains were occasionally observed.
Journal: Thin Solid Films - Volume 518, Issue 1, 2 November 2009, Pages 6–9