Transitions of barium strontium titanate ferroelectric ceramics for different strontium content

Ceramic based barium strontium titanate (BST) solid solutions with the formula Ba1 − xSrxTiO3 are very important candidates for a wide range of device applications. Several doped (Mn and Mg) and undoped samples were prepared by standard solid-state reaction. Special emphasis was put on compositions with x = 0.35 and 0.60, with high potential for applications. The samples were sintered at temperatures in the 1200 ÷ 1260 °C range. Structural X-ray diffraction analysis preformed confirms the perovskite structure. The dielectric parameters were investigated in a wide temperature range between − 150 and 150 °C. The temperature was cyclically changed in both directions, up and down, at a rate of less than 2 °C/min. Both permittivity and dielectric loss were measured at low frequencies, 1 kHz. The peak values of the permittivity are increasing from 2000 to 4000 with the sintering temperature increase. Moreover the dielectric parameters were measured at room temperature in microwave domain (1 ÷ 2 GHz). The Curie temperature of BST samples with x = 0.35 and x = 0.6 is in agreement with the Curie point dependence on Sr content, as we have previously reported.