Comparison of Bi3Fe5O12 film giant Faraday rotators grown on (111) and (001) Gd3Ga5O12 single crystals

Bismuth iron garnet (Bi3Fe5O12, BIG) epitaxial thin films were grown on single crystal (Gd3Ga5O12, GGG) (111) and (001) substrates by rf-magnetron sputtering technique. Processing parameters have been optimized to obtain high deposition rate (2.74 μm/h) and the surface rms roughness less than 10 nm. X-ray diffraction reveals films epitaxial quality: exclusive (111) or (001) orientation with narrow rocking curves and strong in-plane texture. Films possess low optical loss and magneto-optical Faraday rotation (FR) as high as 5 deg/μm at 677 nm wavelength. Comparative analysis of films grown on (111) and (001) substrates clearly shows significant superiority of BIG/GGG(001) film. For this film, the coercive field ∼100 Oe appears to be 2.5 times lower while the optical transmission to be 10% higher than that for BIG/GGG(111) film. Enhanced magneto-optical performance of BIG/GGG(001) films relies upon better accommodation of the film-to-substrate mismatch strain through the tetragonal BIG lattice distortions compared to the rhombohedral one in BIG/GGG(111) films.