![عکس صفحه اول مقاله: Fabrication and characterization of Cu2ZnSnS4 thin films deposited by spray pyrolysis technique Fabrication and characterization of Cu2ZnSnS4 thin films deposited by spray pyrolysis technique](/preview/png/1675854.png)
We have investigated synthesis conditions and some properties of sprayed Cu2ZnSnS4 (CZTS) thin films in order to determine the best preparation conditions for the realization of CZTS based photovoltaic solar cells. The thin films are made by means of spraying of aqueous solutions containing copper chloride, zinc chloride, tin chloride and thiourea on heated glass substrates at various temperatures. In order to optimize the synthesis conditions of the CZTS films, two series of experiments are performed. In the first series the sprayed duration was fixed at 30 min and in the second it is fixed at 60 min. In each series, the substrate temperature was changed from 553°K to 633°K. The X-ray diffraction shows, on one hand, that the best crystallinity was obtained for 613°K as substrate temperature and 60 min as sprayed duration. On the other hand, these CZTS films exhibit the kesterite structure with preferential orientation along the [112] direction. Atomical Force Microscopy was used to determine the grain sizes and the roughness of these CZTS thin film. After the annealing treatment, we estimated the optical band-gap energy of the CZTS thin film exhibiting the best crystallinity as 1.5 eV which is quite close to the optimum value for a solar cell.
Journal: Thin Solid Films - Volume 515, Issue 15, 31 May 2007, Pages 5949–5952