Structural, magneto-static and magneto-dynamic properties of Fe substituted Ni-Mn-In films
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
فناوری نانو (نانو تکنولوژی)
پیش نمایش صفحه اول مقاله

چکیده انگلیسی
Off-stoichiometric Ni-Mn-In films of 500â¯nm thickness were deposited on Si (100) substrate by dc magnetron sputtering at ambient temperature. As-deposited films were annealed ex situ at 550â¯Â°C and 700â¯Â°C for 1â¯h under high vacuum. As-deposited Ni-Mn-In films which were amorphous, exhibited orthorhombic martensite structure upon annealing. The amorphous film was found to be paramagnetic whereas the annealed (martensite) film exhibited weak ferromagnetic behavior. Fe substituted Ni-Mn-In films of the same thickness annealed at 550â¯Â°C exhibited orthorhombic martensite structure, whereas films annealed at 700â¯Â°C exhibited dual phase (cubic L21 austenite and orthorhombic martensite) structure. Martensite Ni-Mn-Fe-In films showed large magnetic moment as compared to the ternary alloy film. Interestingly, films with dual phase structure yielded much higher magnetic moment. Ni-Mn-Fe-In films with higher thicknesses annealed at 700â¯Â°C showed enhanced magnetic moment due to higher L21 phase content in them. Analysis of polar angle variation of resonance field and linewidth of the dual phase Ni-Mn-Fe-In films revealed very low effective perpendicular magnetic anisotropy (3.0â¯Ãâ¯103â¯J/m3) and low Gilbert damping constant (0.009â¯Â±â¯0.001) for the first time. The new results obtained are interpreted in terms of the crystalline nature of the films.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Thin Solid Films - Volume 653, 1 May 2018, Pages 384-389
Journal: Thin Solid Films - Volume 653, 1 May 2018, Pages 384-389
نویسندگان
Rajkumar Modak, M. Manivel Raja, V.V. Srinivasu, A. Srinivasan,