Influence of the substrate texture on the structural and electrochemical properties of sputtered LiCoO2 thin films

LiCoO2 thin films were fabricated on textured and annealed STS304 substrates by direct current magnetron sputtering method. The effects of the substrate texture on the structural and electrochemical properties of the LiCoO2 thin film deposited on both the substrates have been investigated. The crystal structures and surface morphologies of the deposited films were analyzed by X-ray diffractometry (XRD), Raman spectroscopy, and field emission scanning electron microscopy (FE-SEM). Based on the XRD analysis, the LiCoO2 thin film deposited on the textured substrate was found to exhibit (003) preferred orientation, while the film deposited on annealed substrate exhibited (104) preferred orientation. In addition, SEM analysis revealed that the film deposited on the textured substrate showed a smooth morphology. On the other hand, the film deposited on the annealed substrate exhibited a very rough surface morphology, which resulted in a higher surface area. Consequently, the initial discharge capacity of the film deposited on the annealed substrate was higher than that of the film deposited on the textured substrate. The film deposited on the textured substrate exhibited a good cyclic performance compared to the film deposited on the annealed substrate.