Suppression of irradiation hardening in nanoscale V/Ag multilayers
موضوعات مرتبط
مهندسی و علوم پایه مهندسی مواد سرامیک و کامپوزیت
پیش نمایش صفحه اول مقاله
Suppression of irradiation hardening in nanoscale V/Ag multilayers
چکیده انگلیسی
Nanoindentation was used to measure hardness before and after room temperature He ion implantation on sputter-deposited V/Ag multilayers of different layer thickness as well as pure Ag and V. The radiation-induced hardening was found to decrease with decreasing individual layer thickness. No change in hardness after implantation was measured in multilayers with a layer thickness of less than 10 nm, which is of the order of the average spacing of He bubbles. The pure V films exhibit significant hardening due to a dense distribution of 0.8 nm diameter He bubbles, but in the nanocrystalline pure Ag films bubbles grow to a diameter of approximately 20 nm and become ineffective in causing hardening. A model describing layer-thickness-dependent radiation hardening in multilayers was developed by extending the Friedel model to take into account the layer thickness and the He bubble spacing.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Acta Materialia - Volume 59, Issue 16, September 2011, Pages 6331-6340
نویسندگان
, , , , ,