Preparation and characterization of silica/fluorinated acrylate copolymers hybrid films and the investigation of their icephobicity

Inexpensive hydrophobic and icephobic coatings and films were obtained by a simple method. These coatings were prepared by mixing silica sol and fluorinated acrylate copolymers. There was a phase separation process in the film-forming which can provide the excellent performance. Small amount (about 2 wt.%) of fluorinated (methyl) acrylate was used in all of these coatings. The coatings were eco-friendly by using ethanol as the solvent system. Scanning electron microscopy, atomic force microscope, energy dispersive X-ray fluorescence spectrometer, water contact angle, thermal gravimetric analysis and tests of adhesion and hardness had been performed to characterize the morphological feature, chemical composition, hydrophobicity and icephobicity of the surface, thermal stability and mechanical properties of the coatings. The results showed that the films had good hydrophobicity, high thermal stability and excellent mechanical properties of adhesion strength and pencil hardness. Furthermore, by testing their properties of delaying water droplet from icing, it was found that ice formation was delayed for 90 min compared with the glass surface at − 5.6 °C. The hybrid coatings may be suitable for large-scale and practical application owing to its flexibility and simplicity.

► Coatings were prepared by mixing fluorinated acrylate copolymer and silica.
► Mechanical properties and anti-icing performance of the coatings were examined.
► Water contact angle increased with raising SiO2 (sol)/monomers weight ratio.
► Ice formation was delayed for 90 min at − 5.6 °C.