![عکس صفحه اول مقاله: Effect of deflection on the mechanical and optoelectronic properties of indium tin oxide films deposited on polyethylene terephthalate substrates by pulse magnetron sputtering Effect of deflection on the mechanical and optoelectronic properties of indium tin oxide films deposited on polyethylene terephthalate substrates by pulse magnetron sputtering](/preview/png/1671463.png)
In this research, we studied the effect of deflection on the characteristics of an indium tin oxide (ITO) film deposited on a flexible polyethylene terephthalate flexible substrate by pulse magnetron sputtering. The experimental results show that an increase in the ITO film thickness leads to an increase in the residual stress and a decrease in the adhesion. Under power of 80 W, pulse frequency of 10 kHz, pulse reverse time of 2 μs, and ITO film thickness of 100 nm, thin film with an optimized resistivity of 4.5 × 10− 4 Ω-cm, visible light transmittance of more than 84%, and adhesion of class 5B/0 as per the ASTM/ISO standards. Micro-cracking was observed on the ITO film surface when the film thickness was greater than 100 nm and when the deflection was carried out for 100 times. Micro-cracking led to an increase in the residual stress and deterioration in the adhesion properties.
Journal: Thin Solid Films - Volume 517, Issue 5, 1 January 2009, Pages 1701–1705