![عکس صفحه اول مقاله: Study of the moderate-temperature growth process of optical quality synthetic diamond films on quartz substrates Study of the moderate-temperature growth process of optical quality synthetic diamond films on quartz substrates](/preview/png/1672908.png)
Growth of undoped and boron-doped diamond films on quartz substrates at moderate temperature of 500 °C by microwave plasma chemical vapor deposition method was studied in terms of growth rate, surface roughness and optical transmittance. Similar density of diamond seed particles on quartz surfaces seeded mechanically before the deposition process and diamond grains within diamond films grown on those substrates is observed. The growth rate is found similar to that reported for diamond deposited on silicon substrates in the same plasma deposition system, although with substantially higher activation energy. Furthermore, increased level of dopant concentration in the gas mixture resulted in a decrease of the growth rate, while a gradual reduction of the surface roughness occurred at high dopant levels. Overall, the highest measured regular optical transmittance of the undoped diamond film on quartz was 45% at 1100 nm (including quartz absorption), whereas that of boron-doped diamond peaked 5% at 700 nm (tail absorption of boron centers).
Journal: Thin Solid Films - Volume 516, Issue 15, 2 June 2008, Pages 4915–4920